Q&A: Film Thickness Control

By: Rodger Talbert
22. May 2013

 

Q. We are having some trouble controlling the thickness of the powder on our parts. We have some light coat areas in recesses and edges, but we also get orange peel and heavy coating in some other areas. What can we do to control the thickness better? P.T.

 

A. Coating thickness is controlled by the use of a standard set of operating variables that affect film build. There are many variables involved but the critical controls include:
• Gun-to-target distance
• Electrostatic settings (voltage and micro-amps)
• Flow rate and powder velocity
• Number of strokes or dwell time in front of the gun

 

To develop an optimum set of controls you need to do some experimentation and verification. Try full voltage and amperage to start with a medium to low setting on flow rate, average distance (6 inches for manual guns and 12 for automatic guns) two to three passes. Use medium to slow strokes with some overlap of your pattern.

 

For complex shapes, reduce the amperage and voltage and coat difficult areas first. Observe the spray pattern to see how much velocity you have (high velocity is bad) and note how much overspray is generated. If the overspray is low and the coverage is good you are fine. Increase flow if you need more powder, decrease flow if you have a lot of overspray. Establish a standard set up and be consistent.

 

In addition to the gun settings and optimum control, the atmosphere can affect film thickness control. If the humidity is too high the powder will not fluidize or flow very well. If the humidity is too low the powder will behave differently when exposed to an electrostatic charge and potentially produce more rejects for lumps and light coating. The optimum range for humidity is 40 to 60 percent RH.

 

Control of the reclaim powder is important, too. If the powder is recycled in a cyclone recovery system, it will gradually move the particle size distribution higher due to the fact that the cyclone classifies out some of the finer particles. In a module system, the impact on reclaim is the opposite: the particle size distribution will gradually move to a finer overall mean as a result of the accumulation of finer particles. A cartridge module system does not remove any fines and history has demonstrated that 100 percent reclaim will have a finer grind size than virgin powder. To control this, make sure to consume the reclaim and do not let it accumulate. Keep the First Pass Transfer Efficiency at or above 50 percent to make sure that fines do not accumulate.

 

One final and very important control item is the earth ground. If you want film uniformity, control the ground at all times. Clean hooks are imperative to film build control. Control the gun, control the powder and control the atmosphere surrounding your application area. This will give you the best possible film build control. 

 

To read more of Rodger Talbert's answers to readers, click HERE

Comments are reviewed by moderators before they appear to ensure they meet Products Finishing’s submission guidelines.
blog comments powered by Disqus

Suppliers | Products | Experts | News | Articles | Calendar | Process Zones

The Voice of the Finishing Industry Since 1936 Copyright © Gardner Business Media, Inc. 2014

Subscribe | Advertise | Contact Us | All Rights Reserved