Stripping the Anodic Coating
Question: I have several thousand hose fittings that are a machined casting made of 356-T6 aluminum alloy.
Share
Question:
I have several thousand hose fittings that are a machined casting made of 356-T6 aluminum alloy. The parts are anodized and dyed olive drab. The parts in inventory are no longer needed by our customer so I am looking for a way to remove the anodized color and return the parts to their original, un-anodized appearance. We can then return the parts to inventory to sell as an unanodized commercial grade part. The dimensional tolerance on machined diameters is ±0.005". What do you suggest? C.W.
Answer:
I would suggest making up a stripping bath to the following recipe. This bath will readily remove the oxide coating from the parts without any appreciable affect on the aluminum substrate. The size of the tank used (volume of the bath) may depend on the number of batches you are willing to process in order to get all the parts stripped. It may also depend on what kind of container (tank) you have available. I would suggest anything from 50-250 gal in size. I present the recipe two different ways. Both give the same results, so take your pick.
I would recommend placing the parts to be stripped on a rack or fixture made of aluminum or in a stainless steel basket arranged so that they can't touch each other. Immerse the parts for 1-5 min. Determine the stripping time by running a few test parts first. Be aware that as the bath loads up on aluminum oxide the activity of the bath will decrease. The addition of more phosphoric acid will reactivate the bath. Rinse the parts thoroughly after stripping.
RELATED CONTENT
-
How to Apply the 720 Rule to Current Density Anodizing
What can you tell me about the 720 Rule as it applies to current density anodizing? Plating expert Sjon Westre, Ph.D., from Chemeon, answers this question.
-
Deoxidizing Aluminum as a Pretreatment
This important first step can help prepare the metal for subsequent surface finishing.
-
Anodizing for Bonding Applications in Aerospace
Anodizing for pre-prep bonding bridges the gap between metallic and composite worlds, as it provides a superior surface in many applications on aluminum components for bonding to these composites.